| DATA SHEET OF CABLE
FILLING COMPOUND - Grade CU 20 |
| SL No |
Characteristics |
Unit |
Parameters |
Method |
Results |
| |
|
|
|
|
|
| 1 |
COLOUR AND |
--- |
HIGHLY
PASTED, HOMOGENEOUS COMPOUND.DOES NOT OBSCURE COLOUR OF INSULATION. |
VISUAL |
3 - 5 ASTM |
| |
STRUCTURE |
|
& ASTM D 1500 |
Does Not Obscure |
| |
|
|
|
|
| 2 |
APPEARANCE |
--- |
FREE FROM
CONTAMINATION OF FOREIGN MATTERS & SEGREGATED OILS |
VISUAL |
Passes the test |
| |
|
|
|
|
| |
|
|
|
|
|
| 3 |
DENSITY |
gm/cc |
0.89±0.01 |
Volumetric Analysis |
0.88 to 0.90 |
| |
|
|
|
|
|
| 4 |
DROP MELTING POINT |
°C |
85 Minimum |
IP 371 |
85 to 90 |
| |
|
|
|
|
|
| 5 |
VISCOSITY AT 100°C |
Cst |
120±20 |
ASTM - D445 |
105 TO 135 |
| |
|
|
|
|
Min 20 minutes |
| 6 |
FLASH POINT |
°C |
220 minimum |
ASTM - D92 |
235 TO 280 |
| |
(CLEVELAND OPEN CUP) |
|
|
|
|
| |
|
|
|
|
|
| 7 |
Oil Separation |
|
No seperation in 5 days |
IEC 811-5-1 |
Passes the test |
| |
(Stability at 50 °C) |
|
|
|
|
| |
|
|
|
|
|
| 8 |
VOLUME
EXPANSION |
% |
8.0 maximum |
Volumetric Analysis |
Passes the test |
| 9 |
Melting Point |
°C |
Min 85 |
ASTM-D-127 |
> 85 |
| |
|
|
|
|
|
| 10 |
ABSORPTION
IN |
% |
8.0 maximum |
----- |
----- |
| |
MDPE/HDPE |
|
|
|
|
| |
|
|
|
|
|
| 11 |
CONE PENETRATION |
dmm |
60 to 80 |
ASTM - D937 |
65 |
| |
AT 25±0.5°C |
|
|
|
|
| |
|
|
|
|
|
| 12 |
PERMITTIVITY at 1 Mhz |
--- |
2.30 maximum |
ASTM – D150 |
2.28 |
| |
at 23°C |
|
|
|
|
| |
|
|
|
|
|
| 13 |
VOLUME RESISTIVITY AT
500VDC& AT 100°C |
3 |
10 |
|
11 |
| ohm/cm |
1X10 minimum |
ASTM - D1169 |
2.52 x 10 |
| |
|
|
|
|
|
| 14 |
Volumetric Resistance
at 23 °C |
3 |
13 |
|
13 |
| ohm/cm |
1X10 minimum |
ASTM - D1169 |
> 1 x 10 |
| |
|
|
|
|
|
| 15 |
TOXIC & DERMATIC ACTION |
--- |
FREE FROM TOXIC AND DERMATIC
HAZARDS |
STANDARD |
Non Toxic. |
| Packing : 175 Kg Open Mouth M S Barell |
| Note: Cable Filling and Flooding Compound are also
manufactured to customer's desired specifications |
NON-WARRANTY OF RESULTS (Please use after tests and approval) |
| No warranties, express or implied, or warrenties of merchantability or fitness for a particular use,
are made by |
| Chowdhary Udyog with respect to any products described or information set forth herein. Our recommendations |
| for its use are purely based on tests believed reliable. The sample unless
specified as IP is meant for
industrial |
| use only. Since the use is beyond our control we do not guarantee the results whether or not such use is in |
| accordance with directions. It is also understood that the quality and specification of the sample are typical only |
| The information presented herein is based on the evaluation carried out in our in house Lab & on the tests |
| carried out by outside inspection agencies
and the data available therefrom and believed to be correct. |
|
|
|
|
|
|